PA6 MF10
Product name:	Polyamide 6 Nylon PA6 MF10
Filler:	10% mineral
Plastic grade:	Virgin material
Product Model:	PA6-ZJYM10
Application:	Small mechanical parts, housings, handles
Color:	Customized via Pantone color card or RAL color card
Price:	Contact us
MOQ:	Sample: According to customer requirements transactions:1Tons
Country of origin:	China
Payment method:	T/T,L/C,MoneyGram,Western Union
Packing:	25KG/Bag, 1Ton/Pallet

PA6 MF10
Properties	Test conditions	Test unit	Test values
Physical properties
Density	ISO 1183	g/cm³	1.20
Melt volume flow rate
275℃,5 kg	ISO 1183	cm³/10min	90.0
Shrinkage
TD:23℃,72 hrs		%	1.2-1.4
MD:23℃,72 hrs		%	1.1-1.3
Sticky number
96% H2SO4	ISO 307	cm³/g	145
Mechanical properties
Tensile modulus	ISO 527-1-2	MPa	3200
Tensile strength
Succumb	ISO 527-2/50	MPa	70.0
Tensile strain
Fracture	ISO 527-2/5	%	50
Flexural modulus	ISO 178	MPa	3000
Flexural strength	ISO 178	MPa	100
Impact performance
Notched impact strength of Charpy beams
23°C	ISO 179/1eA	KJ/m²	8.0
Charpy beams have no notched impact strength
23°C	ISO 179/1eU		No breakage
Cantilever notched impact strength
23°C	ISO 180/-1A	KJ/m²	8.0
Cantilever beam without notched impact strength
23°C	ISO 180/1U		No breakage
Thermal performance
Melting temperature	ISO 11357-3	°C	221
Electrical properties
Surface resistivity	IEC 60093	ohms	1.0E+13
Volume resistivity	IEC 60093	ohms.cm	1.0E+15
Flame retardant properties
1.60 mm	UL94		HB
Combustion rate	FMVSS 302	mm/min	<100